我们是做国际贸易的,客户询问关于水泥密封剂的问题
我们给客户邮寄的10万,15万粘度HPMC+湖州 HT-58001 可在分散胶粉。
客户请教我们关于添加量,配比的指导意见,产品怎么配比,坑分裂性能更好?
客户提到关于瓦克的一篇文章,(POLYMER MODIFED DRY-MIX TILE ADHESIVES)
http://www.drymt.com/threads/21136/
以下是客户的邮件,供老师们参考。希望能得到老师们的指导意见,谢谢
We are a cement sealant manufacturer. We are ussing now HPMC (20%) and Polymer anti crack(5%) toguether with Portland cement in our mix.
Can you give us your technical opinion about this mix?
[SIZE=12pt]We are using the mix to glue ceramic and Porcelain.
Unfortunately I´m not an engineer like you. I cannot give as much technical information as I will want.
I´m sending you and article of how Cellulose Ether and polymer anti-crack works better together. [/SIZE]
[SIZE=12pt]I hope that will help you to check my point of view.[/SIZE]
我们给客户邮寄的10万,15万粘度HPMC+湖州 HT-58001 可在分散胶粉。
客户请教我们关于添加量,配比的指导意见,产品怎么配比,坑分裂性能更好?
客户提到关于瓦克的一篇文章,(POLYMER MODIFED DRY-MIX TILE ADHESIVES)
http://www.drymt.com/threads/21136/
以下是客户的邮件,供老师们参考。希望能得到老师们的指导意见,谢谢
We are a cement sealant manufacturer. We are ussing now HPMC (20%) and Polymer anti crack(5%) toguether with Portland cement in our mix.
Can you give us your technical opinion about this mix?
[SIZE=12pt]We are using the mix to glue ceramic and Porcelain.
Unfortunately I´m not an engineer like you. I cannot give as much technical information as I will want.
I´m sending you and article of how Cellulose Ether and polymer anti-crack works better together. [/SIZE]
[SIZE=12pt]I hope that will help you to check my point of view.[/SIZE]