摘要：
中文摘要: 干混砂浆是一种由胶凝材料、细集料、矿物掺合料、化学添加剂等均匀混合而成的新型建筑砂浆,具有质量稳定、便于施工、利用废料、利于环保等方面的优越性。目前我国干混砂浆只在少数大城市应用,而且限于少量的特种砂浆,普通干粉砂浆和保温砂浆更少。本文以普通干粉砂浆和外保温砂浆(EPS保温砂浆)作为研究对象,主要进行最佳配合比的设计及性能研究。普通干粉砂浆的研制:首先通过对比试验研究了HPMC和FA掺量对砂浆和易性与抗压强度的影响,确定了HPMC和FA的适宜掺量;进而通过在灰砂比分别为 1∶2,1∶3,1∶4,1∶5,1∶7的普通水泥砂浆中双掺HPMC和FA的方法,确定了强度等级M5.0～M30的砂浆配合比,可以指导不同强度等级普通干粉砂浆的生产。性能测试表明,本文配制的干粉砂浆和易性好,既有足够的抗压强度又有较高的粘结强度。 EPS保温砂浆的研制:首先选取EPS/(C+FA)、FA/(C+FA)和EVA/C为影响因子,以抗压强度和干表观密度为考核指标进行正交试验研究, 运用极差分析及回归分析方法分析正交试验结果,分析得出EPS/(C+FA)是影响抗压强度与干表观密度的主要因素;...
英文摘要: Dry-mixed mortar is a new kind of building mortar that is made by uniformly mixing binding materials,fine aggregates,mineral additives and chemical additives.It has many advantages such as stable quality,constructing expediently,using byproducts and good to environment.Now,our dry-mixed mortar is only using in several big cities,and is limited in specific mortar at small dosage,normal dry powder mortar and insulation mortar are using little,and those two kinds of mortar were studied in this papei,mainly abo...
目录:
第一章 绪论 10-24
1.1 课题研究背景 10-15
1.1.1 墙体材料与建筑砂浆 10-12
1.1.2 干混砂浆的优势 12-13
1.1.3 干混砂浆生产的技术可行性 13-15
1.1.4 干混砂浆关键技术 15
1.2 国内外研究发展现状 15-21
1.2.1 干混砂浆外加剂 16-18
1.2.2 干混砂浆矿物外加剂 18-19
1.2.3 系列标准 19-20
1.2.4 系列产品 20
1.2.5 我国干混砂浆产业化亟待解决的问题 20-21
1.3 国内需求及本文主要研究内容 21-24
1.3.1 国内建筑对商品砂浆的需求 21-23
1.3.2 本文主要研究内容 23-24
第二章 试验研究概况 24-39
2.1 原材料情况及分析 24-31
2.1.1 胶凝材料-水泥 24
2.1.2 细集料-砂 24-25
2.1.3 矿物掺合料-粉煤灰 25-26
2.1.4 化学外加剂-羟丙基甲基纤维素(HPMC) 26-28
2.1.5 绝热材料-聚苯乙烯(EPS)泡沫颗粒 28-29
2.1.6 高分子粘结剂-可再分散性乳胶粉 29-30
2.1.7 增韧抗裂材料-聚丙稀纤维 30-31
2.2 干混砂浆技术要求的确定 31-36
2.2.1 干混砂浆有关的标准规范 31-33
2.2.2 试验方法对强度的影响 33-35
2.2.3 技术指标的确定 35-36
2.3 试验方案及试验方法 36-39
2.3.1 试验方案 36-37
2.3.2 试验方法 37-39
第三章 普通干粉砂浆的组成与性能研究 39-54
3.1 概述 39
3.2 初始配合比设计试验 39-51
3.2.1 纤维素掺量确定 39-42
3.2.2 粉煤灰的掺入方法及掺量的确定 42-44
3.2.3 初始配合比确定试验结果与分析 44-51
3.3 配合比的确定及有关性能测定 51-52
3.3.1 试验内容及方法 51
3.3.2 试验结果及分析 51-52
3.4 本章小结 52-54
第四章 外保温砂浆的组成与性能研究 54-76
4.1 概述 55-56
4.1.1 胶粉聚苯颗粒外墙外保温系统(ETIRS) 55
4.1.2 胶粉聚苯颗粒保温浆料 55-56
4.2 EPS保温砂浆配合比 56-72
4.2.1 试验内容及方法 56
4.2.2 初始配合比确定 56-66
4.2.3 最终配合比确定 66-72
4.3 EPS保温砂浆综合性能试验 72-75
4.3.1 试验内容及方法 72-73
4.3.2 试验结果及分析 73-75
4.4 本章小结 75-76
第五章 细观结构及有关机理分析 76-86
5.1 扫描电镜试验及分析 76-81
5.1.1 试验样品的准备 76-77
5.1.2 试验结果与分析 77-81
5.2 汞压力法测孔试验及分析 81-84
5.2.1 汞压力法原理 82-83
5.2.2 试验结果及分析 83-84
5.3 本章小结 84-86
第六章 总结和展望 86-88
6.1 总结 86-87
6.2 存在问题和展望 87-88
参考文献 88-92
致谢 92
中文摘要: 干混砂浆是一种由胶凝材料、细集料、矿物掺合料、化学添加剂等均匀混合而成的新型建筑砂浆,具有质量稳定、便于施工、利用废料、利于环保等方面的优越性。目前我国干混砂浆只在少数大城市应用,而且限于少量的特种砂浆,普通干粉砂浆和保温砂浆更少。本文以普通干粉砂浆和外保温砂浆(EPS保温砂浆)作为研究对象,主要进行最佳配合比的设计及性能研究。普通干粉砂浆的研制:首先通过对比试验研究了HPMC和FA掺量对砂浆和易性与抗压强度的影响,确定了HPMC和FA的适宜掺量;进而通过在灰砂比分别为 1∶2,1∶3,1∶4,1∶5,1∶7的普通水泥砂浆中双掺HPMC和FA的方法,确定了强度等级M5.0～M30的砂浆配合比,可以指导不同强度等级普通干粉砂浆的生产。性能测试表明,本文配制的干粉砂浆和易性好,既有足够的抗压强度又有较高的粘结强度。 EPS保温砂浆的研制:首先选取EPS/(C+FA)、FA/(C+FA)和EVA/C为影响因子,以抗压强度和干表观密度为考核指标进行正交试验研究, 运用极差分析及回归分析方法分析正交试验结果,分析得出EPS/(C+FA)是影响抗压强度与干表观密度的主要因素;...
英文摘要: Dry-mixed mortar is a new kind of building mortar that is made by uniformly mixing binding materials,fine aggregates,mineral additives and chemical additives.It has many advantages such as stable quality,constructing expediently,using byproducts and good to environment.Now,our dry-mixed mortar is only using in several big cities,and is limited in specific mortar at small dosage,normal dry powder mortar and insulation mortar are using little,and those two kinds of mortar were studied in this papei,mainly abo...
目录:
第一章 绪论 10-24
1.1 课题研究背景 10-15
1.1.1 墙体材料与建筑砂浆 10-12
1.1.2 干混砂浆的优势 12-13
1.1.3 干混砂浆生产的技术可行性 13-15
1.1.4 干混砂浆关键技术 15
1.2 国内外研究发展现状 15-21
1.2.1 干混砂浆外加剂 16-18
1.2.2 干混砂浆矿物外加剂 18-19
1.2.3 系列标准 19-20
1.2.4 系列产品 20
1.2.5 我国干混砂浆产业化亟待解决的问题 20-21
1.3 国内需求及本文主要研究内容 21-24
1.3.1 国内建筑对商品砂浆的需求 21-23
1.3.2 本文主要研究内容 23-24
第二章 试验研究概况 24-39
2.1 原材料情况及分析 24-31
2.1.1 胶凝材料-水泥 24
2.1.2 细集料-砂 24-25
2.1.3 矿物掺合料-粉煤灰 25-26
2.1.4 化学外加剂-羟丙基甲基纤维素(HPMC) 26-28
2.1.5 绝热材料-聚苯乙烯(EPS)泡沫颗粒 28-29
2.1.6 高分子粘结剂-可再分散性乳胶粉 29-30
2.1.7 增韧抗裂材料-聚丙稀纤维 30-31
2.2 干混砂浆技术要求的确定 31-36
2.2.1 干混砂浆有关的标准规范 31-33
2.2.2 试验方法对强度的影响 33-35
2.2.3 技术指标的确定 35-36
2.3 试验方案及试验方法 36-39
2.3.1 试验方案 36-37
2.3.2 试验方法 37-39
第三章 普通干粉砂浆的组成与性能研究 39-54
3.1 概述 39
3.2 初始配合比设计试验 39-51
3.2.1 纤维素掺量确定 39-42
3.2.2 粉煤灰的掺入方法及掺量的确定 42-44
3.2.3 初始配合比确定试验结果与分析 44-51
3.3 配合比的确定及有关性能测定 51-52
3.3.1 试验内容及方法 51
3.3.2 试验结果及分析 51-52
3.4 本章小结 52-54
第四章 外保温砂浆的组成与性能研究 54-76
4.1 概述 55-56
4.1.1 胶粉聚苯颗粒外墙外保温系统(ETIRS) 55
4.1.2 胶粉聚苯颗粒保温浆料 55-56
4.2 EPS保温砂浆配合比 56-72
4.2.1 试验内容及方法 56
4.2.2 初始配合比确定 56-66
4.2.3 最终配合比确定 66-72
4.3 EPS保温砂浆综合性能试验 72-75
4.3.1 试验内容及方法 72-73
4.3.2 试验结果及分析 73-75
4.4 本章小结 75-76
第五章 细观结构及有关机理分析 76-86
5.1 扫描电镜试验及分析 76-81
5.1.1 试验样品的准备 76-77
5.1.2 试验结果与分析 77-81
5.2 汞压力法测孔试验及分析 81-84
5.2.1 汞压力法原理 82-83
5.2.2 试验结果及分析 83-84
5.3 本章小结 84-86
第六章 总结和展望 86-88
6.1 总结 86-87
6.2 存在问题和展望 87-88
参考文献 88-92
致谢 92